Construction reference technology 1. Mix Group A (clear varnish) and Group B (aluminum powder) in proportion, stir evenly, and then proceed with construction, spraying, and brushing. 2. Sandblasting the steel surface to a grade of 2.5. 3. The dry film thickness should be controlled between 40um and 60um. When the coated equipment is used for the first time, it should be gradually heated up to the working temperature to avoid sudden heating that may cause blistering and peeling of the paint film. 5. Theoretical dosage is 100g/m2 (calculated based on a dry film thickness of 50um).
Composition, performance, and purpose 300 # Silver High Temperature Resistant Paint is formulated with self drying synthetic resin and various aluminum powders. Room temperature quick drying, good adhesion, high temperature and corrosion resistance, capable of withstanding high temperatures up to 300 ℃. This paint is suitable for use as a heat-resistant coating on metal surfaces.